| Título : | Caracterização química e metalográfica dos aços inoxidáveis de implantes removidos de pacientes |
| Autor(es): | Silva, Elison da Fonseca e Oliveira, Luiz Fernando Cappa de |
| Resumo: | OBJETIVO: Este trabalho estudou a composição química e metalográfica (microestrutura, tamanho de grão, teor de inclusões) de aços inoxidáveis austeníticos, desenvolvidos para aplicações como biomateriais, utilizados na fabricação de implantes ortopédicos. MÉTODO: Foram analisados doze implantes removidos de pacientes afetados por quadro inflamatório. As análises químicas foram desenvolvidas pelas técnicas Espectrometria de Emissão Ótica e Microanálise por Dispersão de Energia (EDS) e o tamanho de grão foi determinado por microscopia ótica e Microscopia Eletrônica de Varredura (MEV) conforme norma ASTM E 1382 97. RESULTADOS: Observou-se que, todos os implantes apresentavam tamanho de grão superior ao recomendado pela norma, constatou-se também a presença de ferrita delta em dez dos doze implantes removidos, que de acordo com a norma ASTM F138-92 não deveriam ser percebidas microscopicamente com um aumento de 100 vezes. CONCLUSÕES: Em oito casos existe forte indicação de que as inflamações foram desencadeadas pela corrosão por pite. Nivel de Evidência III, Revisão sistemática de Estudos . |
| Resumen : | Objective: This study examines the chemical and metallogra-phic composition (microstructure, grain size, inclusion content) of austenitic stainless steel developed as biomaterials for used in the manufacture of orthopedic implants. Method: An analysis was carried out of twelve implants removed from patients affected by inflammation. Chemical analyses were carried out using Opti-cal Emission Spectrometry and Energy Dispersive Microanalysis (EDS), and the grain size was determined by optical microscopy and scanning electron microscopy (SEM) according to ASTM Standard E 1382 97. Results: It was observed that all the implants had a larger grain size than is recommended by the Standard. The presence of delta ferrite was also observed in ten of the twelve implants removed, which according to ASTM Standard F138-92, should not be perceived microscopically under magnification of 100x. Conclusions: In eight cases, there is a strong indication that the inflammation was triggered by pitting corrosion. Level of Evidence: Level III, Systematic review of studies. |
| Palabras clave : | Aços inoxidáveis Próteses e implantes Materiais biocompatíveis Corrosão Stainless steel Prostheses and implants Biocompa- tible materials Corrosion |
| CNPq: | - |
| Idioma: | por |
| País: | Brasil |
| Editorial : | - |
| Sigla de la Instituición: | - |
| Clase de Acesso: | Acesso Aberto |
| DOI: | http://dx.doi.org/10.1590/S1413-78522011000500003 |
| URI : | https://repositorio.ufjf.br/jspui/handle/ufjf/8613 |
| Fecha de publicación : | 2011 |
| Aparece en las colecciones: | Artigos de Periódicos |
Los ítems de DSpace están protegidos por licencias Creative Commons, con todos los derechos reservados, a menos que se indique lo contrario.