Estudo dos parâmetros de emissão laser de vidros fosfatos dopados com nanocristais de ZnTe e co-dopados com íons de Yb3+

Abstract

In this work, we have proposed a new glass matrix, called PZABP, with nominal composition 60P205 . 15ZnO . 5A/203 . 10Ba0 . 10Pb0, in mol %, nanostructured with ZnTe semiconductor nanocrystals and doped with Yb3+ ions, then, we analized its availability to photonics devices application like high power lasers, optical fiber lasers, ultra-short pulses lasers and tunable lasers in the infrared region. The samples were produced by fusion method, being made two sets. One, PZABP + xYb, was doped with Yb3+ ions at various concentrations from 0% to 10%, in wt%.The other one, PZABP + 1ZnTe + xYb, was doped with semiconductors nanocrystals of ZnTe and Yb3+ ions at concentrations from 0% to 5%, in wt%. The optical properties of the samples and the interactions between neighbors Yb3+ ions and between semiconductors nanocrystals of ZnTe and Yb3+ ions were studied by Optical Absorption, Photoluminescence and Time Resolved Photoluminescence techniques. Thermal Lens Spectroscopy and Heat Volumetric Capacity, also know as pc, were used to characterize the thermal properties of the samples. The main parameters that avail the performance laser and the threshold action laser were estimated by the determination of absorption and emission cross section of the Yb3+ ions when they are inserted in this matrix. The PZABP glass matrix showed to be an excellent host material to Yb3+ ions because it present a large optical window, it is tolerant to high dopants concentration and not showed Yb3+ clusters. Important parameters like lifetime and quantum efficience showed values comparable to others found in the literature. It was verified that the presence of ZnTe nanocrystals had enhanced the emission of the Yb3+ ions, indicating that have occurred energy transfer between ZnTe nanocrystals and Yb3+ ions. Thermal properties have presented interesting values to applications that involved superheated environment. The high thermal diffusivity and high thermal conductivity allow the sample to dissipate the heat quickly. The low variation of the optical path with the temperature (ds/dT) indicate that the laser beam not strongly deviates into the optical cavity. The laser performance parameters obtained are comparable to the other glass matrix found in the literature, although the presence of the ZnTe nanocrystals seems to prejudice these parameters. According with the results found and the improvement that could be done, we have conclude that the glass matrix PZABP nanostructured with semiconductores nanocrystals of ZnTe and doped with Yb3+ ions is a viable material to application in high power photonics devices materials.