Mechanical properties of orthodontic wires on ceramic brackets associated with low friction ligatures

Abstract

Introduction: Few studies investigated the mechanical properties of orthodontic wires on ceramic brackets associated the ligatures. Objective: This study aimed to compare the load-deflection of orthodontic wires with round section of 0.016” made of stainless steel (SS), nickel-titanium (NiTi) and glass fiber-reinforced polymer composite (GFRPC). Material and method: Sixty specimens obtained from 10 sectioned pre-contoured arches (TP Orthodontics), were divided into 3 groups of 20 according to each type of material (1 esthetic-type wire and 2 not esthetic) and length of 50 mm. The methodology consisted of a 3-point bending test using esthetic ceramic brackets (INVU, TP Orthodontics, Edgewise, 0.022”x 0.025”) as points of support. The tensile tests were performed on a mechanical test machine, at a speed of 10 mm/min, deflection of 1 mm, 2 mm and 3 mm. Friedman’s Non Parametric Multiple comparisons test was used (P<0.05). Result: The nickel-titanium wire presented smaller load/ deflection compared with stainless steel. GFRPC wires had lower strength values among all groups evaluated (P<.05). The steel wire showed permanent deformation after 3 mm deflection, NiTi wire demonstrated memory effect and the esthetic type had fractures with loss of strength. Conclusion: It can be concluded that steel wires have high strength values, requiring the incorporation of loops and folds to reduce the load / deflection. NiTi and GFRPC wires produced low levels of force, however the esthetic wire was shown to fracture and break.