Efeito de ligaduras elásticas sobre a viabilidade celular e produção de óxido nítrico em células J744

Abstract

Although the physical properties of elastic ligatures have been the subject of several studies, the biocompatibility of these materials has not been well documented in the literature. This study was an in vitro investigation of the cellular viability of the murine macrophage J774 cell line in the presence of elastomeric ligatures of different brands and colors, and of nitric oxide (NO) production of these cells both, under the presence of such ligatures, and under the influence of a proinflammatory cytokine: gamma-interferon. After sterilization with ethylene oxide, 6 chains of ligatures of 3 different brands (Morelli, GAC e TP) and colors (silver and transparent) were used at each study time. The 96-well culture plates used in the experiment were divided in 2 halves. The first was filled with J774 cells resuspended in supplemented RPMI medium, along with the chains of each kind of ligature and control cells. The second half was filled with another 6 chains of the same kinds of ligatures, kept in J774 cell cultures in supplemented RPMI medium, along with 10μl of IFN-γ (5 ng/ml) and control cells. The plates were incubated at 24, 48, and 72 hours. The MTT [3 – (4,5-dimethylthiazol-2-yl) – diphenyl tetrazolium bromide] technique was used for cellular viability assessment, and the supernatants were collected for NO production analysis with the Griess method. Kruskal-Wallis and Mann-Whitney tests were used to analyze the results. Cellular viability in the elastomeric groups was higher at the final time point in relation to the control group. However, 3 elastomeric groups (silver Morelli, transparent Morelli and silver GAC) showed significant proliferation after 72 hours. TP-ligature-exposed cells had the same behavior of controls, no significant changes in cellular viability and NO production being found. Although silver Morelli ligatures led to higher NO production, the other types of ligatures did not significantly affect NO production, as compared to control cells. In the presence of IFN-γ, Morelli and GAC ligatures led to a significant reduction of cellular viability after 48 hours. Yet a viability mean higher than that seen in control cells was observed for all ligatures after 72 hours, with transparent GAC showing significant proliferation. Cells exposed to TP ligatures had the same behavior of controls, although silver TP ligatures led to lower viability at 24 hours. Nitric oxide production was significantly greater in all groups at the final time point in relation to the initial time point. The transparent Morelli and silver and transparent GAC showed the smallest NO production at the 3 study time points.