Componentes calcináveis para implantes Cone Morse: análise da desadaptação entre pilar / implante

Abstract

The system of dental implants present in one or more components, and the correct interrelationship, settling and passive biomechanical strength, defining the strength / vulnerability of the same to the forward occlusal and bacterial factors.Objective: To evaluate the defects associated to laboratory processing of abutments of unique body to the system of Cone Morse implants. Methods: We used 20 Cone Morse implants SIN brand, prosthetic components 10 and 10 calcinable not calcinable. After the laboratory processes the sets were subjected to scanning electron microscopy (SEM) of the pillar / implant interface, for qualitative and quantitative analysis of the generated misfit. The samples were taken to alternated thermal cycles (1000 – 50 and 550) and mechanical fatigue (500,000 - 120 N/cm2) and again was carried out by SEM. The results were compared by statistical analysis Mean-Whitmann (P>0,05). Results: The test group (G1) showed the highest initial values, averaging 34.55 and 11.17 micrometres for subdivisions A (casting) and B (porcelain application) respectively. The B subdivision of the test group showed the greatest change after tests, averaging 19.28 mm of increasing prosthetic misfit. The G1.A subdivisions, G2.A, G2.B showed a tendency to decrease the mismatch of -1.03 micrometres - 1.64 micrometres and -0.49 micrometres respectively. Pillars Cone Morse calcinable not present with high stability and low rate misfits. For the test group it can be said that the casting process clearly created the largest expansion and mismatches of structures. The porcelain sintering process under test, created a reduction of the mismatch measure, however this increased again after the tests in the laboratory. For the control group, there was the maintenance of rates of minor mismatches to 10 micrometres limit, and with downward trend after the tests. Conclusion: Cone Morse castable pillars proved to be unfavorable on the biomechanics, and the casting process generated the biggest misfits.